Product Description：Apec® 1745 is an easy-release polycarbonate resin (PC)
Material Type：Polycarbonate
Manufacturer：Covestro - Polycarbonates
Supply Regions：North America, Latin America, Asia Pacific, Africa and the Middle East, Europe
Characteristics：Good release properties, steam sterilizable
Applications：Films, Pharmaceuticals, Medical devices, Valves/valve components, Medical/nursing supplies, Medical packaging
Certifications：ISO 10993, USP Class VI
Processing Method：Injection Molding
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Density | 23°C | 1.17 | g/cm³ | ISO 1183 | |
| Melt Flow Rate (MFR) | 330°C/2.16 kg | 17 | g/10 min | ISO 1133 | |
| Shrinkage - Flow | 2.00 mm | 0.85 | % | ISO 294-4 | |
| Water Absorption - Saturated | 23°C | 0.30 | % | ISO 62 | |
| Water Absorption - Equilibrium | 23°C, 50% RH | 0.12 | % | ISO 62 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Tensile Modulus | 23°C | 2400 | MPa | ISO 527-1/1 | |
| Tensile Stress - Yield | 23°C | 70.0 | MPa | ISO 527-2/50 | |
| Tensile Strain - Yield | 23°C | 6.8 | % | ISO 527-2/50 | |
| Nominal Tensile Strain at Break | 23°C | > 50 | % | ISO 527-2/50 | |
| Flexural Modulus | 23°C | 2400 | MPa | ISO 178 | |
| Flexural Stress | 23°C | 120 | MPa | ISO 178 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Izod Unnotched Impact Strength | -30°C | Unbroken | -- | ISO 179/1eU | |
| Izod Unnotched Impact Strength | 23°C | Unbroken | -- | ISO 179/1eU |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Ball Indentation Hardness | -- | 120 | MPa | ISO 2039-1 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Heat Deflection Temperature Under Load | 0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B | |
| Heat Deflection Temperature Under Load | 1.8 MPa, Unannealed | 148 | °C | ISO 75-2/A | |
| Vicat Softening Temperature | -- | 170 | °C | ISO 306/B120 | |
| Linear Thermal Expansion Coefficient - Flow | 23 to 55°C | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+16 | ohms | IEC 60093 | |
| Volume Resistivity | 23°C | 1.0E+17 | ohms·cm | IEC 60093 | |
| Dielectric Strength | 23°C, 1.00 mm | 35 | kV/mm | IEC 60243-1 | |
| Relative Permittivity | 23°C, 100 Hz | 3.00 | -- | IEC 60250 | |
| Relative Permittivity | 23°C, 1 MHz | 2.90 | -- | IEC 60250 | |
| Dissipation Factor | 23°C, 100 Hz | 1.0E-3 | -- | IEC 60250 | |
| Dissipation Factor | 23°C, 1 MHz | 8.0E-3 | -- | IEC 60250 | |
| Tracking Index - Solution A | -- | 250 | V | IEC 60112 | |
| Tracking Index - Solution B | -- | 125 | V | IEC 60112 | |
| Electrolytic Corrosion | 23°C | A1 | -- | IEC 60426 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| UL Flammability Rating | 1.5 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index | 2.0 mm | 850 | °C | IEC 60695-2-12 | |
| Limiting Oxygen Index | -- | 25 | % | ISO 4589-2 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Refractive Index | -- | 1.578 | -- | ISO 489 | |
| Transmittance | 1000 µm | 88.0 | % | ISO 13468-2 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Drying Temperature - Dry Air Dryer | -- | 130 | °C | -- | |
| Drying Time - Dry Air Dryer | -- | 2.0 to 3.0 | hr | -- | |
| Recommended Maximum Moisture Content | -- | < 0.020 | % | -- | |
| Recommended Shot Size | -- | 30 to 70 | % | -- | |
| Barrel Rear Temperature | -- | 290 to 300 | °C | -- | |
| Barrel Middle Temperature | -- | 300 to 310 | °C | -- | |
| Barrel Front Temperature | -- | 310 to 320 | °C | -- | |
| Nozzle Temperature | -- | 320 to 330 | °C | -- | |
| Processing (Melt) Temperature | -- | 320 to 340 | °C | -- | |
| Mold Temperature | -- | 110 to 130 | °C | -- | |
| Back Pressure | -- | 5.00 to 15.0 | MPa | -- | |
| Vent Depth | -- | 0.025 to 0.075 | mm | -- |
Product Description：CALIBRE™ 2060-3 is a high transparency polycarbonate resin (PC)
Material Type：Polycarbonate Resin
Manufacturer：Trinseo
Supply Regions：North America, Asia Pacific
Characteristics：High impact resistance, High heat resistance, Steam sterilizable, Autoclave sterilizable, High clarity, Ethylene oxide sterilizable, Biocompatible
Applications：Medical, Nursing supplies
Certifications：ISO 10993
Processing Method：Film Extrusion, Injection Molding
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Density / Specific Gravity | -- | 1.20 | g/cm³ | ASTM D792 / ISO 1183 | |
| Melt Flow Rate (MFR) | 300°C/1.2 kg | 3.5 | g/10 min | ASTM D1238 / ISO 1133 | |
| Shrinkage - Flow | -- | 0.50 to 0.70 | % | ASTM D955 / ISO 294-4 | |
| Water Absorption - Saturated | 23°C | 0.32 | % | ISO 62 | |
| Water Absorption - Equilibrium | 23°C, 50% RH | 0.12 | % | ISO 62 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Tensile Modulus | -- | 2480 | MPa | ASTM D638 | |
| Tensile Strength - Yield | -- | 60.0 | MPa | ASTM D638 | |
| Tensile Strength - Break | -- | 72.0 | MPa | ASTM D638 | |
| Elongation - Yield | -- | 6.0 | % | ASTM D638 | |
| Elongation - Break | -- | 140 | % | ASTM D638 | |
| Flexural Modulus | -- | 2410 | MPa | ASTM D790 | |
| Flexural Strength | -- | 96.5 | MPa | ASTM D790 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Izod Notched Impact Strength | -30°C | 14 | kJ/m² | ISO 179/1eA | |
| Izod Notched Impact Strength | 23°C | 55 | kJ/m² | ISO 179/1eA | |
| Charpy Notched Impact Strength | 23°C | 960 | J/m | ASTM D256 | |
| Instrumented Dart Impact | 23°C, Total energy | 93.8 | J | ASTM D3763 | |
| Tensile Impact Strength | -- | 630 | kJ/m² | ASTM D1822 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Rockwell Hardness - M Scale | -- | 74 | -- | ASTM D785 | |
| Rockwell Hardness - R Scale | -- | 118 | -- | ASTM D785 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Heat Deflection Temperature Under Load | 0.45 MPa, Annealed | 146 | °C | ASTM D648 / ISO 75-2/B | |
| Heat Deflection Temperature Under Load | 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A | |
| Vicat Softening Temperature | -- | 151 | °C | ASTM D1525 | |
| Linear Thermal Expansion Coefficient - Flow | -- | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Refractive Index | -- | 1.586 | -- | ASTM D542 / ISO 489 | |
| Transmittance | -- | 87.0 to 91.0 | % | ASTM D1003 | |
| Haze | -- | < 1.00 | % | ASTM D1003 |
| Property Item | Test Conditions | Nominal Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Drying Temperature | -- | 120 | °C | -- | |
| Drying Time | -- | 4.0 | hr | -- | |
| Processing (Melt) Temperature | -- | 290 to 330 | °C | -- | |
| Mold Temperature | -- | 80 to 110 | °C | -- |