We act as an agent for sales and production of high-end medical engineering plastics, providing safe and high-performance basic materials for medical products. Our product range covers various types to meet the special requirements of different medical devices.

Product Features:

- Complete range of material types

- Stable quality

- Excellent product performance

- Good biocompatibility

- Suitable for various molding processes

Technical Parameter Summary Table

Compound RL004 Performance Data Sheet

Product Basic Information

Product Description: LNP LUBRICOMP RL004 is a compound based on Nylon 66 resin.

Material Type: Polyamide 66

Manufacturer: SABIC

Supply Region: North America, Latin America

Additives: PTFE Lubricant: 20%

Characteristics: Good wear resistance, lubrication

Applications: Electrical/Electronic Applications, Electronic Displays, Oil/Gas Products, Appliances, Textile Applications, Pharmaceuticals

Processing Method: Injection Molding

Physical Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Density / Specific Gravity--1.25g/cm³ASTM D792
Shrinkage - Flow24 hours1.0 - 3.0%ASTM D955
Water Absorption24 hr, 50% RH0.79%ASTM D570
Water Absorption - Equilibrium73°F (23°C), 50% RH1.2%ISO 62

Mechanical Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Tensile Modulus--3200MPaASTM D638
Tensile Strength - Break--71.0MPaASTM D638
Elongation - Break--6.7%ASTM D638
Flexural Modulus1.97 in (50.0 mm) Span2680MPaASTM D790
Flexural Modulus--2700MPaISO 178
Flexural Stress--90.0MPaISO 178
Coefficient of Friction - Dynamic--0.32-ASTM D3702
Coefficient of Friction - Static--0.21-ASTM D3702
Wear Factor--3.2E+610^-8 mm³/N•mASTM D3702

Impact Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Izod Notched Impact Strength73°F (23°C)35J/mASTM D256
Izod Unnotched Impact73°F (23°C)600J/mASTM D4812
Instrumented Dart Impact - Total Energy73°F (23°C)4.00JASTM D3763

Hardness

Property Item Test Conditions Rated Value Unit Test Method Remarks
Rockwell Hardness - M Scale--56-ASTM D785
Rockwell Hardness - R Scale--110-ASTM D785

Thermal Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Heat Deflection Temperature Under Load66 psi (0.45 MPa), Unannealed, 0.126 in (3.20 mm)239°CASTM D648
Heat Deflection Temperature Under Load66 psi (0.45 MPa), Unannealed, 0.157 in (4.00 mm), 2.52 in (64.0 mm) Span201°CISO 75-2/Bf
Heat Deflection Temperature Under Load264 psi (1.8 MPa), Unannealed, 0.126 in (3.20 mm)71.0°CASTM D648
Heat Deflection Temperature Under Load264 psi (1.8 MPa), Unannealed, 0.157 in (4.00 mm), 2.52 in (64.0 mm) Span68.0°CISO 75-2/Af
Linear Thermal Expansion Coefficient - Flow-22 to 86°F (-30 to 30°C)9.0E-5cm/cm/°CASTM D696
Linear Thermal Expansion Coefficient - Transverse-22 to 86°F (-30 to 30°C)8.8E-5cm/cm/°CASTM D696

Processing Parameters

Property Item Test Conditions Rated Value Unit Test Method Remarks
Drying Temperature--80°C--
Drying Time--4.0hr--
Recommended Maximum Moisture Content--0.15 - 0.25%--
Barrel Rear Temperature--265 - 275°C--
Barrel Middle Temperature--280 - 295°C--
Barrel Front Temperature--295 - 305°C--
Processing (Melt) Temperature--275 - 290°C--
Mold Temperature--80 - 95°C--
Back Pressure--0.200 - 0.300MPa--
Screw Speed--30 - 60rpm--

Compound RF006 Performance Data Sheet

Product Basic Information

Product Description: LNP THERMOCOMP RF006 is a compound based on Nylon 66 resin.

Material Type: Polyamide 66

Manufacturer: SABIC

Supply Region: North America, Latin America

Filler: Glass Fiber 30% by weight

Characteristics: Reinforced Material

Applications: Appliances, Automotive External Parts, Electronic Displays, Pharmaceuticals

Processing Method: Injection Molding

Physical Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Density / Specific Gravity--1.40g/cm³ASTM D792
Shrinkage - Flow24 hours0.30 - 0.60%ASTM D955
Water Absorption24 hr, 50% RH0.64%ASTM D570
Water Absorption - Equilibrium73°F (23°C), 50% RH0.94%ISO 62

Mechanical Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Tensile Modulus--11400MPaASTM D638
Tensile Strength - Break--167MPaASTM D638
Elongation - Break--2.4%ASTM D638
Flexural Modulus1.97 in (50.0 mm) Span9700MPaASTM D790
Flexural Stress--233MPaISO 178
Flexural Stress - Yield1.97 in (50.0 mm) Span243MPaASTM D790
Flexural Stress - Break1.97 in (50.0 mm) Span242MPaASTM D790

Impact Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Izod Notched Impact Strength73°F (23°C)67J/mASTM D256
Izod Notched Impact Strength73°F (23°C)6.0kJ/m²ISO 180/1A
Izod Unnotched Impact Strength73°F (23°C)44kJ/m²ISO 180/1U
Instrumented Dart Impact - Total Energy73°F (23°C)6.00JASTM D3763
Instrumented Dart Impact--2.00JISO 6603-2

Thermal Properties

Property Item Test Conditions Rated Value Unit Test Method Remarks
Heat Deflection Temperature66 psi (0.45 MPa), Unannealed, 0.157 in (4.00 mm), 2.52 in (64.0 mm) Span255°CISO 75-2/Bf
Heat Deflection Temperature264 psi (1.8 MPa), Unannealed, 0.126 in (3.20 mm)246°CASTM D648
Heat Deflection Temperature264 psi (1.8 MPa), Unannealed, 0.157 in (4.00 mm), 2.52 in (64.0 mm) Span236°CISO 75-2/Af
Linear Thermal Expansion Coefficient - Flow-22 to 86°F (-30 to 30°C27cm/cm/°CASTM D696
Linear Thermal Expansion Coefficient - Transverse-22 to 86°F (-30 to 30°C)98cm/cm/°CASTM D696

Processing Parameters

Property Item Test Conditions Rated Value Unit Test Method Remarks
Drying Temperature--80°C--
Drying Time--4.0hr--
Recommended Maximum Moisture Content--0.15 - 0.25%--
Barrel Rear Temperature--265 - 275°C--
Barrel Middle Temperature--280 - 295°C--
Barrel Front Temperature--295 - 305°C--
Processing (Melt) Temperature--280 - 305°C--
Mold Temperature--95 - 110°C--
Back Pressure--0.200 - 0.300MPa--
Screw Speed--30 - 60rpm--