We act as an agent for sales and production of high-end medical engineering plastics, providing safe and high-performance base materials for medical products. Our product range covers various types to meet the special requirements of different medical devices.
Product Features:
- Complete range of material types
- Stable quality
- Excellent product performance
- Good biocompatibility
- Suitable for various molding processes
Product Description: VESTAKEEP® D4 G is a natural-colored, high-viscosity polyetheretherketone (PEEK) designed for removable and fixed dental crown and bridge restorations.
Material Type: Polyetheretherketone (PEEK)
Manufacturer: Evonik Industries AG
Supply Regions: North America, Europe
Characteristics: Biocompatible, good chemical resistance, high viscosity
Applications: Dental applications
Certifications: ISO 10993 Part 3, 5, 10, 11, 18, USP Class VI
Appearance: Natural color
Processing Methods: Extrusion, Injection Molding
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Density | 73°F (23°C) | 1.30 | g/cm³ | ISO 1183 | |
| Melt Volume Rate (MVR) | 380°C/5.0 kg | 12.0 | cm³/10min | ISO 1133 | |
| Water Absorption - Saturated | 73°F (23°C) | 0.40 | % | ISO 62 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Tensile Modulus | -- | 3500 | MPa | ISO 527-2 | |
| Tensile Stress - Yield | -- | 96.0 | MPa | ISO 527-2 | |
| Tensile Strain - Yield | -- | 5.0 | % | ISO 527-2 | |
| Tensile Strain - Break | -- | > 10 | % | ISO 527-2 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Izod Notched Impact Strength | 73°F (23°C), Complete Break | 8.0 | kJ/m² | ISO 179/1eA | |
| Izod Unnotched Impact Strength | 73°F (23°C) | Unbroken | -- | ISO 179/1eU |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Heat Deflection Temperature | 66 psi (0.45 MPa), Unannealed | 210 | °C | ISO 75-2/B | |
| Heat Deflection Temperature | 264 psi (1.8 MPa), Unannealed | 155 | °C | ISO 75-2/A | |
| Vicat Softening Temperature | -- | 335 | °C | ISO 306/A | |
| Vicat Softening Temperature | -- | 305 | °C | ISO 306/B | |
| Melting Temperature | -- | 340 | °C | ISO 11357-3 | |
| Linear Thermal Expansion Coefficient - Flow | 73 to 131°F (23 to 55°C) | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Processing (Melt) Temperature | -- | 380 to 400 | °C | -- | |
| Mold Temperature | -- | 160 to 200 | °C | -- |
Product Description: PEEK-OPTIMA® polymers are high-performance biomaterials that provide advanced solutions for implant manufacturing.
Material Type: Polyetheretherketone (PEEK)
Manufacturer: Invibio Inc.
Supply Regions: North America, Europe
Characteristics: Radiation, steam, ethylene oxide sterilizable, hydrolysis resistance, high strength, good chemical resistance, biocompatibility, good sterilizability, good wear resistance
Applications: Human implants, medical, nursing supplies
Certifications: DMF Unrated, ISO 10993, USP Class VI, FDA Unrated, MAF Unrated
Appearance: Natural color
Processing Methods: Extrusion, Compression Molding, Injection Molding
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Density / Specific Gravity | -- | 1.29 | g/cm³ | ASTM D792 | |
| Shrinkage Rate - Flow | 0.118 in (3.00 mm) | 1.2 | % | ASTM D955 | |
| Water Absorption | 73°F (23°C), 24 hr | 0.50 | % | ISO 62 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Tensile Stress - Yield | -- | 100 | MPa | ISO 527-2/1B/50 | |
| Tensile Strain - Break | -- | 20 | % | ISO 527-2/1B/50 | |
| Flexural Modulus | -- | 4000 | MPa | ISO 178 | |
| Flexural Stress | -- | 170 | MPa | ISO 178 | |
| Compressive Strength | -- | 118 | MPa | ASTM D695 | |
| Shear Modulus | -- | 1300 | MPa | ASTM D732 | |
| Shear Strength | -- | 53.1 | MPa | ASTM D732 | |
| Poisson's Ratio | -- | 0.40 | -- | ASTM E132 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Izod Notched Impact Strength | -- | 63 | J/m | ASTM D256 | |
| Izod Unnotched Impact Strength | -- | Unbroken | -- | ASTM D256 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Rockwell Hardness (M Scale) | -- | 99 | -- | ASTM D785 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Melting Temperature | -- | 340 | °C | DSC | |
| Linear Thermal Expansion Coefficient - Flow | -- | 4.7E-5 | cm/cm/°C | ASTM D696 | |
| Linear Thermal Expansion Coefficient - Flow | -- | 1.1E-4 | cm/cm/°C | ASTM D696 |
| Property Item | Test Conditions | Rated Value | Unit | Test Method | Remarks |
|---|---|---|---|---|---|
| Drying Temperature | -- | 150 | °C | -- | |
| Drying Time | -- | 3.0 | hr | -- | |
| Recommended Maximum Moisture Content | -- | 0.10 | % | -- | |
| Recommended Maximum Recycled Material Ratio | -- | 0 | % | -- | |
| Barrel Rear Temperature | -- | 350 to 355 | °C | -- | |
| Barrel Middle Temperature | -- | 355 to 365 | °C | -- | |
| Barrel Front Temperature | -- | 360 to 370 | °C | -- | |
| Nozzle Temperature | -- | 365 to 375 | °C | -- | |
| Mold Temperature | -- | 160 to 200 | °C | -- | |
| Injection Pressure | -- | 7.00 to 14.0 | MPa | -- | |
| Packing Pressure | -- | 4.00 to 10.0 | MPa | -- | |
| Back Pressure | -- | 0.200 to 5.00 | MPa | -- | |
| Screw Speed | -- | 50 to 100 | rpm | -- | |
| Clamping Force | -- | 5.0 to 8.0 | kN/cm² | -- | |
| Screw Length-Diameter Ratio | -- | 18.0:1.0 to 24.0:1.0 | -- | -- | |
| Screw Compression Ratio | -- | 2.0 : 1.0 to 3.0 : 1.0 | -- | -- |